产品特性:高耐热PC | 是否进口:否 | 产地:美国 |
厂家(产地):SABIC | 牌号:XHT4141 | 销售方式:品牌经销 |
类型:标准料 | 品名:PC | 加工级别:注塑级 |
特性级别:透明级、 耐高温 | 用途级别:汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 | 品牌:LEXAN |
产品规格:25KG/包 |
SABIC PC LEXAN XHT4141高耐热透明PC
Density / Specific Gravity | |||
-- | 1.20 | g/cm? | ASTM D792 |
-- | 1.21 | g/cm? | ISO 1183 |
Melt Mass-Flow Rate (MFR) (330°C/2.16 kg) | 25 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR) (330°C/2.16 kg) | 24 | cm?/10min | ISO 1133 |
Molding Shrinkage - Flow (3.20 mm) | 0.60 to 0.95 | % | Internal Method |
Water Absorption | ISO 62 | ||
Saturation, 23°C | 0.50 | % | |
Equilibrium, 23°C, 50% RH | 0.25 | % |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 3 | 2730 | MPa | ASTM D638 |
-- | 2750 | MPa | ISO 527-1/1 |
Tensile Strength | |||
Yield 4 | 77.0 | MPa | ASTM D638 |
Yield | 78.0 | MPa | ISO 527-2/50 |
Break 4 | 69.0 | MPa | ASTM D638 |
Break | 67.0 | MPa | ISO 527-2/50 |
Charpy Notched Impact Strength 8 | ISO 179/1eA | ||
-30°C | 9.0 | kJ/m? | |
23°C | 11 | kJ/m? |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed, 3.20 mm | 174 | °C | ASTM D648 |
0.45 MPa, Unannealed, 4.00 mm, 64.0 mm Span 10 | 173 | °C | ISO 75-2/Bf |
1.8 MPa, Unannealed, 3.20 mm | 165 | °C | ASTM D648 |
1.8 MPa, Unannealed, 4.00 mm, 64.0 mm Span 10 | 162 | °C | ISO 75-2/Af |