品牌:SOLEF | 是否进口:否 | 产地:美国 |
厂家(产地):美国苏威 | 牌号:6020 | 销售方式:品牌经销 |
类型:标准料 | 品名:PVDF | 加工级别:涂覆级 |
产品规格:25KG/包 | 产品特性:电池级PVDF |
美国苏威高粘锂电池级粉PVDF Solef 6020
Density / Specific Gravity | 1.75 to 1.80 | g/cm | ASTM D792 |
Melt Mass-Flow Rate (MFR)(230°C/21.6 kg) | <2.0 | g/10 min | ASTM D1238 |
Water Absorption(24 hr, 23°C) | <0.040 | % | ASTM D570 |
Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus2(23°C, 2.00 mm) | 1600 to 1700 | MPa | ASTM D638 |
Tensile Strength3 | ASTM D638 | ||
Yield, 23°C, 2.00 mm | 53.0 to 57.0 | MPa | |
Break, 23°C, 2.00 mm | 25.0 to 50.0 | MPa | |
Tensile Elongation3 | ASTM D638 | ||
Yield, 23°C, 2.00 mm | 5.0 to 10 | % | |
Break, 23°C, 2.00 mm | 15 to 50 | % |
Thermal | Nominal Value | Unit | Test Method |
Glass Transition Temperature | -40.0 | °C | ASTM D4065 |
Melting Temperature | 171 to 175 | °C | ASTM D3418 |
Peak Crystallization Temperature (DSC) | 133 to 138 | °C | ASTM D3418 |
Crystallization Heat | 47.0 to 52.0 | J/g | ASTM D3417 |
Heat of Fusion | 57.0 to 66.0 | J/g | ASTM D3417 |
Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | > 1.0E+14 | ohms | ASTM D257 |
Volume Resistivity | > 1.0E+14 | ohms·cm | ASTM D257 |
模塑成型 一般先将PVDF粒料放在烘箱或预热炉中预热,预热温度215~235摄氏度,然后将预热好的物料加到事先预热好的180~195摄氏度的模具中,在14MPa下施压、保压,保压时间视熔融和流动所需时间而定。厚壁制品必须保压冷却到90摄氏度以下才能脱模,以避免制品产生真空气泡或发生变形。
(5)传递模塑成型 一般先采用挤出机塑化,然后将物料输送到储料缸中,通过柱塞泵将储料缸中的物料注入到模具里,并保压冷却。不管是模塑成型还是传递成型,主要用来生产体积较大、壁厚较厚的产品。
(5)其它加工方法 加工PVDF还可采用浸渍、共挤出、符合等加工工艺。