品牌:MAKROLON | 是否进口:否 | 产地:德国 |
厂家(产地):科思创 | 牌号:6267X | 销售方式:品牌经销 |
类型:标准料 | 品名:PC | 加工级别:注塑级 |
产品规格:25KG/包 | 产品特性:阻燃抗紫外 |
原包科思创PC MAKROLON 6267X阻燃抗紫外线
Density(23°C) | 1.20 | g/cm | ISO 1183 |
Apparent (Bulk) Density3 | 0.64 | g/cm | ISO 60 |
Melt Mass-Flow Rate (MFR)(300°C/1.2 kg) | 20 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR)(300°C/1.2 kg) | 19 | cm/10min | ISO 1133 |
Tensile Modulus(23°C) | 2450 | MPa | ISO 527-2/1 |
Tensile Stress | ISO 527-2/50 | ||
Yield, 23°C | 67.0 | MPa | |
Break, 23°C | 65.0 | MPa | |
Tensile Strain | ISO 527-2/50 | ||
Yield, 23°C | 6.0 | % | |
Break, 23°C | 120 | % | |
Nominal Tensile Strain at Break(23°C) | > 50 | % | ISO 527-2/50 |
Flexural Modulus5(23°C) | 2400 | MPa | ISO 178 |
Flexural Stress5 | ISO 178 | ||
23°C | 97.0 | MPa | |
3.5% Strain, 23°C | 74.0 | MPa | |
Flexural Strain at Flexural Strength6(23°C) | 6.9 | % | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength7 | ISO 179/1eA | ||
-30°C, Complete Break | 12 | kJ/m | |
23°C, Partial Break | 60 | kJ/m |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 134 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 122 | °C | ISO 75-2/A |
Flame Rating(1.5 mm) | V-0 | UL 94 | |
Glow Wire Flammability Index | IEC 60695-2-12 | ||
0.75 mm | 960 | °C | |
1.5 mm | 960 | °C | |
3.0 mm | 960 | °C |