品牌:MAKROLON | 是否进口:否 | 产地:德国 |
厂家(产地):科思创 | 牌号:2408 | 销售方式:品牌经销 |
类型:标准料 | 品名:PC | 加工级别:注塑级 |
特性级别:高流动 | 用途级别:医用级 | 产品规格:25KG/包 |
产品特性:低粘医疗级 |
原包科思创低粘医疗级PC MAKROLON 2408
Density(23°C) | 1.20 | g/cm | ISO 1183 |
Apparent (Bulk) Density3 | 0.66 | g/cm | ISO 60 |
Melt Mass-Flow Rate (MFR)(300°C/1.2 kg) | 20 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR)(300°C/1.2 kg) | 19 | cm/10min | ISO 1133 |
Tensile Modulus(23°C) | 2350 | MPa | ISO 527-2/1 |
Tensile Stress | ISO 527-2/50 | ||
Yield, 23°C | 65.0 | MPa | |
Break, 23°C | 70.0 | MPa | |
Tensile Strain | ISO 527-2/50 | ||
Yield, 23°C | 6.3 | % | |
Break, 23°C | 120 | % | |
Nominal Tensile Strain at Break(23°C) | > 50 | % | ISO 527-2/50 |
Tensile Creep Modulus | ISO 899-1 | ||
1 hr | 2200 | MPa | |
1000 hr | 1900 | MPa | |
Flexural Modulus5(23°C) | 2350 | MPa | ISO 178 |
Flexural Stress5 | ISO 178 | ||
23°C | 96.0 | MPa | |
3.5% Strain, 23°C | 72.0 | MPa | |
Flexural Strain at Flexural Strength6(23°C) | 7.0 | % | ISO 178 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength7 | ISO 179/1eA | ||
-30°C, Complete Break | 14 | kJ/m | |
23°C, Partial Break | 65 | kJ/m |