| 产品特性：阻燃PBT | 是否进口：否 | 产地：美国 |
| 厂家(产地)：SABIC | 牌号：310SE0 | 销售方式：品牌经销 |
| 类型：标准料 | 品名：PBT | 加工级别：注塑级 |
| 特性级别：阻燃级 | 用途级别：汽车部件、 电子电器部件、 运动器材、 家电部件、 电动工具配件 | 品牌：VALOX |
| 产品规格：25KG/包 |
SABIC VALOX 310SE0阻燃5VA级PBT
Density / Specific Gravity | 1.40 | g/cm? | ASTM D792, *** 1183 |
Specific Volume | 0.710 | cm?/g | ASTM D792 |
Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 8.6 | g/10 min | ASTM D1238 |
Melt Volume-Flow Rate (MVR) (250°C/2.16 kg) | 8.0 | cm?/10min | *** 1133 |
Molding Shrinkage | Internal Method | ||
Across Flow 2 | 0.90 to 1.9 | % | |
Flow 2 | 1.1 to 1.8 | % | |
Across Flow : 0.750 to 2.30 mm | 1.0 to 1.7 | % | |
Flow : 0.750 to 2.30 mm | 0.90 to 1.6 | % | |
Flow : 3.20 mm | 1.5 to 2.3 | % | |
Across Flow : 2.30 to 4.60 mm | 1.6 to 2.4 | % | |
Flow : 2.30 to 4.60 mm | 1.5 to 2.3 | % | |
Water Absorption | *** 62 | ||
Saturation, 23°C | 0.36 | % | |
Equilibrium, 23°C, 50% RH | 0.080 | % | |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness (R-Scale) | 120 | *** 2039-2 | |
Ball Indentation Hardness (H 358/30) | 105 | MPa | *** 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | |||
-- 3 | 2820 | MPa | ASTM D638 |
-- | 2800 | MPa | *** 527-1/1 |
Tensile Strength | |||
Yield 4 | 58.0 | MPa | ASTM D638 |
Yield | 58.0 | MPa | *** 527-2/50 |
Break 4 | 52.0 | MPa | ASTM D638 |
Break | 40.0 | MPa | *** 527-2/50 |
Tensile Elongation | |||
Yield 4 | 5.0 | % | ASTM D638 |
Yield | 5.0 | % | *** 527-2/50 |
Break 4 | 18 | % | ASTM D638 |
Break | 18 | % | *** 527-2/50 |
Flexural Modulus | |||
50.0 mm Span 5 | 2620 | MPa | ASTM D790 |
-- 6 | 2600 | MPa | *** 178 |
Flexural Stress | |||
-- 6, 7 | 90.0 | MPa | *** 178 |
Yield, 50.0 mm Span 5 | 101 | MPa | ASTM D790 |
Taber Abrasion Resistance (1000 Cycles, 1000 g, CS-17 Wheel) | 19.0 | mg | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | |||
-30°C 8 | 4.0 | kJ/m? | *** 179/1eA |
23°C 8 | 8.0 | kJ/m? | *** 179/1eA |
23°C | 5.0 | kJ/m? | *** 179/2C |