| 品牌：LATAMID | 是否进口：否 | 产地：意大利 |
| 厂家(产地)：LATI | 牌号：12G/50 | 销售方式：品牌经销 |
| 类型：标准料 | 品名：PA12 | 加工级别：注塑级 |
| 产品规格：25KG/包 | 产品特性：高刚PA12 |
LATAMID 12 G/50高刚50%玻纤PA12
| Density | 1.45g/cc | 0.0524lb/in | |
| Linear Mold Shrinkage, Flow | 0.0035-0.0055cm/cm | 0.0035-0.0055in/in | |
| Linear Mold Shrinkage, Transverse | 0.0075-0.010cm/cm | 0.0075-0.010in/in | |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 55.0MPa @Temperature 150 °C | 7980psi @Temperature 302 °F | |
| 80.0MPa @Temperature 120 °C | 11600psi @Temperature 248 °F | ||
| 90.0MPa @Temperature 90.0 °C | 13100psi @Temperature 194 °F | ||
| 110MPa @Temperature 60.0 °C | 16000psi @Temperature 140 °F | ||
| 150MPa @Temperature 23.0 °C | 21800psi @Temperature 73.4 °F | ||
| Elongation at Break | 4.5 % @Temperature 23.0 °C | 4.5 % @Temperature 73.4 °F | |
| 6.2 % @Temperature 60.0 °C | 6.2 % @Temperature 140 °F | ||
| 6.7 % @Temperature 90.0 °C | 6.7 % @Temperature 194 °F | ||
| 7.7 % @Temperature 120 °C | 7.7 % @Temperature 248 °F | ||
| 8.6 % @Temperature 150 °C | 8.6 % @Temperature 302 °F | ||
| Elongation at Yield | 6.0 % @Temperature 23.0 °C | 6.0 % @Temperature 73.4 °F | |
| Tensile Modulus | 3.30GPa @Temperature 150 °C | 479ksi @Temperature 302 °F | |
| 4.30GPa @Temperature 120 °C | 624ksi @Temperature 248 °F | ||
| 5.10GPa @Temperature 90.0 °C | 740ksi @Temperature 194 °F | ||
| 6.30GPa @Temperature 60.0 °C | 914ksi @Temperature 140 °F | ||
| 10.5GPa @Temperature 23.0 °C | 1520ksi @Temperature 73.4 °F | ||
| Charpy Impact Unnotched | 10.0J/cm | 47.6ft-lb/in | |
| Charpy Impact, Notched | 1.80J/cm | 8.57ft-lb/in | |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 120°C | 248°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 190°C | 374°F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 185°C | 365°F | |
| Vicat Softening Point | 180°C @Load 5.00 kg | 356°F @Load 11.0 lb | |