| 品牌：ULTRAMID | 是否进口：否 | 产地：德国 |
| 厂家(产地)：德国巴斯夫 | 牌号：TKR4350 | 销售方式：品牌经销 |
| 类型：标准料 | 品名：PA6T | 加工级别：注塑级 |
| 产品规格：25KG/包 | 产品特性：高抗冲PPA |
经销德国巴斯夫PA6/6T Ultramid T KR 4350高抗冲高刚PPA
Density | 1.16 | -- | g/cm | *** 1183 |
Apparent (Bulk) Density | 0.70 | -- | g/cm | |
Molding Shrinkage | *** 294-4 | |||
Across Flow | 1.1 | -- | % | |
Flow | 0.85 | -- | % | |
Water Absorption | *** 62 | |||
Saturation, 23°C | 6.5 to 7.5 | -- | % | |
Equilibrium, 23°C, 50% RH | 1.6 to 2.0 | -- | % | |
Viscosity Number(96% H2SO4 (Sulphuric Acid)) | 130 | -- | cm/g | *** 307 |
Mold Shrinkage - constrained3 | 0.60 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus | 3100 | 3100 | MPa | *** 527-1 |
Tensile Stress(Yield) | 80.0 | 70.0 | MPa | *** 527-2/50 |
Tensile Strain(Yield) | 5.0 | -- | % | *** 527-2/50 |
Nominal Tensile Strain at Break | 8.0 | -- | % | *** 527-2/50 |
Tensile Creep Modulus4(1000 hr) | -- | 2300 | MPa | *** 899-1 |
Flexural Modulus | 2900 | -- | MPa | *** 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | *** 179/1eA | |||
-30°C | 6.0 | -- | kJ/m | |
23°C | 8.0 | -- | kJ/m | |
Charpy Unnotched Impact Strength | *** 179/1eU | |||
-30°C | 130 | -- | kJ/m | |
23°C | 140 | -- | kJ/m | |
Notched Izod Impact Strength(23°C) | 8.0 | -- | kJ/m | *** 180/A |
| Thermal | Dry | Conditioned | Unit | Test Method |
Deflection Temperature Under Load(1.8 MPa, Unannealed) | 95.0 | -- | °C | *** 75-2/A |
Melting Temperature | 295 | -- | °C | *** 11357-3 |
CLTE - Flow(23 to 55°C) | 6.0E-5 to 8.0E-5 | -- | cm/cm/°C | *** 11359-2 |
Specific Heat | 1500 | -- | J/kg/°C | |
Thermal Conductivity | 0.23 | -- | W/m/K | DIN 52612 |
Maximum Service Temperature - short cycle operation | 250 | -- | °C | |
Temperature Index - at 50% loss of tensile strength | IEC 60216 | |||
--5 | 130 | -- | °C | |
--6 | 110 | -- | °C |