| 品牌：Ultrason | 是否进口：否 | 产地：德国 |
| 厂家(产地)：德国巴斯夫 | 牌号：S2010G4 | 品名：PSU |
| 用途级别：汽车部件、电子电器部件、家电部件、电动工具配件 | 产品规格：25KG/包 | 产品特性：高刚PSU |
| 销售方式：品牌经销 | 类型：标准料 | 加工级别：注塑级 |
| 特性级别：增强级、***、抗化学性、高强度、高刚性 |
德国巴斯夫PSU Ultrason S2010G4玻纤增强20%高刚PSU
Density | 1.38 | g/cm | *** 1183 |
Melt Volume-Flow Rate (MVR)(360°C/10.0 kg) | 40 | cm/10min | *** 1133 |
Molding Shrinkage | *** 294-4 | ||
Across Flow | 0.52 | % | |
Flow | 0.31 | % | |
Water Absorption | *** 62 | ||
Saturation, 23°C | 0.70 | % | |
Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Hardness | Nominal Value | Unit | Test Method |
Ball Indentation Hardness | 170 | MPa | *** 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus(23°C) | 6600 | MPa | *** 527-1 |
Tensile Stress(Break, 23°C) | 115 | MPa | *** 527-2 |
Tensile Strain(Break, 23°C) | 2.9 | % | *** 527-2 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | *** 179 | ||
-30°C | 8.0 | kJ/m | |
23°C | 8.0 | kJ/m | |
Charpy Unnotched Impact Strength | *** 179 | ||
-30°C | 55 | kJ/m | |
23°C | 50 | kJ/m | |
Notched Izod Impact Strength | *** 180 | ||
-30°C | 8.0 | kJ/m | |
23°C | 8.0 | kJ/m |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load(1.8 MPa, Unannealed) | 184 | °C | *** 75-2/A |
CLTE - Flow | 2.6E-5 | cm/cm/°C | |
RTI Elec | UL 746B | ||
1.6 mm | 160 | °C | |
3.0 mm | 160 | °C | |
RTI Imp | UL 746B | ||
1.6 mm | 140 | °C | |
3.0 mm | 140 | °C | |
RTI Str | UL 746B | ||
1.6 mm | 160 | °C | |
3.0 mm | 160 | °C |
| Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
Electric Strength | 46 | kV/mm | IEC 60243-1 |
Dielectric Constant | IEC 60250 | ||
100 Hz | 3.50 | ||
1 MHz | 3.50 | ||
Dissipation Factor | IEC 60250 | ||
100 Hz | 1.0E-3 | ||
1 MHz | 6.0E-3 | ||
Comparative Tracking Index | 125 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating | UL 94 | ||
1.6 mm | V-1 | ||
3.0 mm | V-0 |
| Notes |