| 品牌：Ultramid | 是否进口：否 | 产地：德国 |
| 厂家(产地)：德国巴斯夫 | 牌号：1503-2 | 销售方式：品牌经销 |
| 类型：标准料 | 品名：PA66 | 加工级别：注塑级 |
| 产品规格：25KG/包 | 产品特性：热稳定增强 |
代理巴斯夫热稳定PA66 Ultramid 1503-2 nf2004增强33%GF
Density / Specific Gravity | 1.40 | -- | g/cm | ASTM D792,*** 1183 |
Molding Shrinkage - Flow(3.18 mm) | 0.30 | -- | % |
Water Absorption | ||||
Saturation | 5.7 | -- | % | ASTM D570 |
Saturation, 23°C | 5.7 | -- | % | *** 62 |
Equilibrium, 50% RH | 1.7 | -- | % | ASTM D570 |
Equilibrium, 23°C, 50% RH | 1.7 | -- | % | *** 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus(23°C) | 10800 | 7400 | MPa | *** 527-2 |
Tensile Strength | ||||
Break, 23°C | 193 | -- | MPa | ASTM D638 |
Break, 23°C | 210 | 145 | MPa | *** 527-2 |
Tensile Elongation | ||||
Break, 23°C | 3.0 | -- | % | ASTM D638 |
Break, 23°C | 3.0 | 5.0 | % | *** 527-2 |
Flexural Modulus | ||||
23°C | 8280 | -- | MPa | ASTM D790 |
23°C | 9900 | 6300 | MPa | *** 178 |
Flexural Strength(23°C) | 276 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | *** 179 | |||
-30°C | 11 | 11 | kJ/m | |
23°C | 12 | 15 | kJ/m |
Deflection Temperature Under Load | ||||
0.45 MPa, Unannealed | 297 | -- | °C | ASTM D648 |
0.45 MPa, Unannealed | 264 | -- | °C | *** 75-2/B |
1.8 MPa, Unannealed | 252 | -- | °C | ASTM D648 |
1.8 MPa, Unannealed | 255 | -- | °C | *** 75-2/A |
Peak Melting Temperature | 260 | -- | °C | ASTM D3418,*** 3146 |
代理巴斯夫热稳定PA66 Ultramid 1503-2 nf2004增强33%GF