批发科思创PC MAKROLON 6165X高流动阻燃
Flame Rating(1.2 mm) | V-0 | UL 94 | |
Glow Wire Flammability Index | IEC 60695-2-12 | ||
1.5 mm | 960 | °C | |
3.0 mm | 960 | °C |
Density(23°C) | 1.20 | g/cm | ISO 1183 |
Apparent (Bulk) Density3 | 0.64 | g/cm | ISO 60 |
Melt Mass-Flow Rate (MFR)(300°C/1.2 kg) | 30 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR)(300°C/1.2 kg) | 28 | cm/10min | ISO 1133 |
Tensile Modulus(23°C) | 2350 | MPa | ISO 527-2/1 |
Tensile Stress | ISO 527-2/50 | ||
Yield, 23°C | 65.0 | MPa | |
Break, 23°C | 55.0 | MPa | |
Tensile Strain | ISO 527-2/50 | ||
Yield, 23°C | 6.0 | % | |
Break, 23°C | 120 | % | |
Nominal Tensile Strain at Break(23°C) | > 50 | % | ISO 527-2/50 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength5 | ISO 179/1eA | ||
-30°C, Complete Break | 12 | kJ/m | |
23°C, Complete Break | 15 | kJ/m |
Notched Izod Impact Strength5 | ISO 180/A | ||
-30°C, Complete Break | 11 | kJ/m | |
23°C, Partial Break | 15 | kJ/m | |
Multi-Axial Instrumented Impact Energy(23°C) | 45.0 | J | ISO 6603-2 |
Multi-Axial Instrumented Impact Peak Force(23°C) | 4800 | N | ISO 6603-2 |
Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 136 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 124 | °C | ISO 75-2/A |
Vicat Softening Temperature | 143 | °C | ISO 306/B50 |