代理德国朗盛55%GF玻纤PBT/PET POCAN T3150XF
| Rheological properties |
| C | Melt volume-flow rate | 270 °C; 5 kg | cm/(10 min) | *** 1133-1 | 30 |
| C | Molding shrinkage, parallel | 60x60x2; 280 °C / MT 90°C; 600 bar | % | *** 294-4 | 0.3 |
| C | Molding shrinkage, transverse | 60x60x2; 280 °C / MT 90°C; 600 bar | % | *** 294-4 | 0.8 |
| Post- shrinkage, parallel | 60x60x2; 120 °C; 4 h | % | *** 294-4 | 0.1 |
| Post- shrinkage, transverse | 60x60x2; 120 °C; 4 h | % | *** 294-4 | 0.1 |
| C | Charpy impact strength | 23 °C | kJ/m | *** 179-1eU | 50 |
| C | Charpy impact strength | -30 °C | kJ/m | *** 179-1eU | 50 |
| C | Charpy notched impact strength | 23 °C | kJ/m | *** 179-1eA | <10 |
| C | Charpy notched impact strength | -30 °C | kJ/m | *** 179-1eA | <10 |
| Izod impact strength | 23 °C | kJ/m | *** 180-1U | 45 |
| Izod impact strength | -30 °C | kJ/m | *** 180-1U | 45 |
| C | Melting temperature | 10 °C/min | °C | *** 11357-1,-3 | 225-260 |
| C | Temperature of deflection under load | 1.80 MPa | °C | *** 75-1,-2 | 210 |
| C | Temperature of deflection under load | 0.45 MPa | °C | *** 75-1,-2 | 230 |
| Vicat softening temperature | 50 N; 120 °C/h | °C | *** 306 | 210 |
| C | Coefficient of linear thermal expansion, parallel | 23 to 55 °C | 10-4/K | *** 11359-1,-2 | 0.1 |
| C | Coefficient of linear thermal expansion, transverse | 23 to 55 °C | 10-4/K | *** 11359-1,-2 | 0.6 |