批发美国SABIC耐冲抗蠕变PC/PBT XENOY X4820
| 比重 |
|
|
|
| -- | 1.25 | g/cm | ASTM D792 |
| -- | 1.26 | g/cm | *** 1183 |
| 熔流率（熔体流动速率）(250°C/5.0 kg) | 10 | g/10 min | ASTM D1238 |
| 溶化体积流率（MVR）(265°C/5.0 kg) | 12.0 | cm/10min | *** 1133 |
| 收缩率 - 流动(3.20 mm) | 0.95 到 1.1 | % | 内部方法 |
| 吸水率 |
|
| *** 62 |
| 饱和, 23°C | 0.42 | % | *** 62 |
| 平衡, 23°C, 50% RH | 0.14 | % | *** 62 |
| 简支梁缺口冲击强度9(23°C) | 60 | kJ/m | *** 179/1eA |
| 悬壁梁缺口冲击强度 |
|
|
|
| -30°C | 150 | J/m | ASTM D256 |
| 23°C | 700 | J/m | ASTM D256 |
| -30°C10 | 15 | kJ/m | *** 180/1A |
| 23°C11 | 55 | kJ/m | *** 180/1A |
| 装有测量仪表的落镖冲击(23°C, Total Energy) | 60.0 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 |
|
|
|
| 1.8 MPa, 未退火, 3.20 mm | 98.0 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距12 | 94.0 | °C | *** 75-2/Af |