原包沙伯基础11%玻纤增强PBT/PC XENOY 1760
| 比重 | 1.30 | g/cm? | ASTM D792, *** 1183 |
| 溶化体积流率（MVR） (265°C/5.0 kg) | 12.0 | cm?/10min | *** 1133 |
| 收缩率 |
|
| 内部方法 |
| 流动 : 3.20 mm | 0.40 到 0.60 | % | 内部方法 |
| 横向流动 : 3.20 mm | 0.40 到 0.60 | % | 内部方法 |
| 吸水率 |
|
| *** 62 |
| 饱和, 23°C | 0.50 | % | *** 62 |
| 平衡, 23°C, 50% RH | 0.15 | % | *** 62 |
| 简支梁缺口冲击强度 9(23°C) | 16 | kJ/m? | *** 179/1eA |
| 悬壁梁缺口冲击强度 |
|
|
|
| -30°C | 85 | J/m | ASTM D256 |
| 23°C | 95 | J/m | ASTM D256 |
| -30°C 10 | 3.0 | kJ/m? | *** 180/1A |
| 23°C 11 | 3.0 | kJ/m? | *** 180/1A |
| 装有测量仪表的落镖冲击 |
|
| ASTM D3763 |
| -30°C, Energy at Peak Load | 3.00 | J | ASTM D3763 |
| -30°C, Total Energy | 3.00 | J | ASTM D3763 |
| -20°C, Energy at Peak Load | 4.00 | J | ASTM D3763 |
| 23°C, Total Energy | 8.00 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
|---|
| 载荷下热变形温度 |
|
|
|
| 1.8 MPa, 未退火, 6.40 mm | 115 | °C | ASTM D648 |
| 1.8 MPa, 未退火, 64.0 mm 跨距 12 | 104 | °C | *** 75-2/Af |
原包沙伯基础11%玻纤增强PBT/PC XENOY 1760