| 品牌：RYTON | 是否进口：否 | 产地：美国 |
| 厂家(产地)：索尔维 | 牌号：XE5430NA | 品名：PPS |
| 产品规格：25KG/包 | 产品特性：热稳定PPS | 销售方式：品牌经销 |
| 类型：标准料 | 加工级别：注塑级 | 特性级别：增韧级、增强级、热稳定性、高抗冲 |
经销索尔维30%GF热稳定PPS RYTON XE5430NA
| Density | 1.52g/cc | 0.0549lb/in | Method A; ISO 1183 |
| Water Absorption | 0.020 % @Time 86400 sec | 0.020 % @Time 24.0 hour | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 165MPa | 23900psi | ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | ASTM D638 |
| Flexural Strength | 240MPa | 34800psi | ASTM D790 |
| Flexural Modulus | 9.00GPa | 1310ksi | ISO 178 |
| Compressive Strength | 215MPa | 31200psi | ASTM D695 |
| Izod Impact, Notched (ISO) | 13.0kJ/m | 6.19ft-lb/in | Notch A; ISO 180 |
| Izod Impact, Unnotched (ISO) | 65.0kJ/m | 30.9ft-lb/in | ISO 180 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+16ohm-cm | 1.00e+16ohm-cm | ASTM D257 |
| Dielectric Constant | 3.7 @Frequency 1000 Hz | 3.7 @Frequency 1000 Hz | ASTM D150 |
| 3.7 @Frequency 1.00e+6 Hz | 3.7 @Frequency 1.00e+6 Hz | ASTM D150 | |
| Dielectric Strength | 20.0kV/mm | 508kV/in | ASTM D149 |
| Dissipation Factor | 0.0020 @Frequency 1000 Hz | 0.0020 @Frequency 1000 Hz | ASTM D150 |
| 0.0020 @Frequency 1.00e+6 Hz | 0.0020 @Frequency 1.00e+6 Hz | ASTM D150 | |
| Arc Resistance | 125sec | 125sec | ASTM D495 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 10.0m/m-°C @Temperature 100 - 200 °C | 5.56in/in-°F @Temperature 212 - 392 °F | ISO 11359-2 |
| 20.0m/m-°C @Temperature -50.0 - 50.0 °C | 11.1in/in-°F @Temperature -58.0 - 122 °F | ISO 11359-2 | |
| CTE, linear, Transverse to Flow | 55.0m/m-°C @Temperature -50.0 - 50.0 °C | 30.6in/in-°F @Temperature -58.0 - 122 °F | ISO 11359-2 |
| 90.0m/m-°C @Temperature 100 - 200 °C | 50.0in/in-°F @Temperature 212 - 392 °F | ISO 11359-2 | |
| Thermal Conductivity | 0.270W/m-K | 1.87BTU-in/hr-ft-°F | ISO 8302 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm | V-0 @Thickness 0.0630 in | UL 94 |
PPS平均分子量为0.4-0.5万，密度为1.3-1.8克每立方厘米，pps有十分有意的热性能。用玻纤增强后的热性能指标更高，它的连续使用温度达400度，pps的热稳定性优良，加热至500度时重量损失不明显，至700度时才会完全降解，它的力学性能随温度的升高下降很少，在232度经5000h的热老化后，其抗弯强度和抗拉强度还能保持50%以上。pps的抗拉强度、抗弯强度等性能在工程塑料中属中等水平，而伸长率和冲击强度却很低，因此在受力构件中使用pps通常加入添加剂，如玻纤、碳纤、填料等来增强其力学性能，pps通过这种改性后，主要力学性能，如抗拉性能、抗弯性能、压缩和冲击强度均有大幅度提高，伸长率却有下降，改性后的pps能在长期负荷和热负荷的作用下保持高的力学性能和尺寸稳定性，因而可应用于温度高的受力环境中。