| 品牌：TORELINA | 是否进口：否 | 产地：日本 |
| 厂家(产地)：日本东丽 | 牌号：A400M-X05 | 品名：PPS |
| 产品规格：25KG/包 | 产品特性：低翘曲PPS | 销售方式：品牌经销 |
| 类型：标准料 | 加工级别：注塑级 | 特性级别：增强级、***、高强度、高刚性 |
东丽60%增强低翘曲PPS TORELINA A400M-X05
Density(23°C) | 1.82 | g/cm | *** 1183 |
Molding Shrinkage2 | Internal Method | ||
Across Flow : 3.00 mm | 0.75 | % | |
Flow : 3.00 mm | 0.20 | % | |
Water Absorption(24 hr, 23°C) | 0.020 | % | *** 62 |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness(R-Scale) | 122 | *** 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Stress(23°C) | 165 | MPa | *** 527-2 |
Tensile Strain(Break, 23°C) | 1.1 | % | *** 527-2 |
Flexural Modulus(23°C) | 18500 | MPa | *** 178 |
Flexural Stress(23°C) | 250 | MPa | *** 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 9.0 | kJ/m | *** 179 |
Charpy Unnotched Impact Strength(23°C) | 25 | kJ/m | *** 179 |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature(1.8 MPa, Unannealed) | 260 | °C | *** 75-2/A |
Melting Temperature | 278 | °C | *** 11357-3 |
CLTE | *** 11359-2 | ||
Flow | 1.8E-5 | cm/cm/°C | |
Transverse | 3.0E-5 | cm/cm/°C |
PPS用于电子电器工业可占30%，它适合于环境温度高于200℃的高温电器元件；可制造发电机和发动机上的点涮、电涮托架、启动器线圈、屏蔽罩及叶片等；在电视机上，可用于高电压外壳及插座、接线柱及端子板等；在电子工业、制造变压器、阻流圈及继电器的骨架和壳体，集成电路载体；利用高频性能，制造H级绕线架和微调电容器等。
（3）机械工业：用于壳体、结构件、***件及密封材料，具体有泵体、阀门、轴承、轴承支架、活塞环及齿轮等。
在机械工业各个领域当使用尼龙（PA）、POM、（PET）和聚砜（PSU）都有缺陷式不能达到技术要求，而使用聚酰亚胺（PI）聚醚醚酮（PEEK）和聚酰胺-酰亚胺（PAI）又太高，选择使用PPS应是较理想的工程塑料。