| 品牌：TORELINA | 是否进口：否 | 产地：日本 |
| 厂家(产地)：日本东丽 | 牌号：A305MD1 | 品名：PPS |
| 产品规格：25KG/包 | 产品特性：高刚PPS | 销售方式：品牌经销 |
| 类型：标准料 | 加工级别：注塑级 | 特性级别：增强级、***、高强度、高刚性 |
日本东丽高强度高刚PPS TORELINA A305MD1
Density(23°C) | 1.75 | g/cm | *** 1183 |
Molding Shrinkage2 | Internal Method | ||
Across Flow : 3.00 mm | 0.75 | % | |
Flow : 3.00 mm | 0.16 | % | |
Water Absorption(24 hr, 23°C) | 0.020 | % | *** 62 |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness(R-Scale) | 122 | *** 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Stress(23°C) | 180 | MPa | *** 527-2 |
Tensile Strain(Break, 23°C) | 1.3 | % | *** 527-2 |
Flexural Modulus(23°C) | 17000 | MPa | *** 178 |
Flexural Stress(23°C) | 260 | MPa | *** 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 8.0 | kJ/m | *** 179 |
Charpy Unnotched Impact Strength(23°C) | 40 | kJ/m | *** 179 |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature(1.8 MPa, Unannealed) | 260 | °C | *** 75-2/A |
Melting Temperature | 278 | °C | *** 11357-3 |
CLTE | *** 11359-2 | ||
Flow | 1.8E-5 | cm/cm/°C | |
Transverse | 3.0E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
Electric Strength | 24 | kV/mm | IEC 60243-1 |
Dielectric Constant3(23°C, 1 MHz) | 5.00 | IEC 60250 | |
Dissipation Factor3(23°C, 1 MHz) | 2.0E-3 | IEC 60250 | |
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating(0.35 mm) | V-0 | UL 94 |
PPS在负荷下的耐蠕变性好，硬度高；***性高，其1000转时的磨耗量仅为0.04g，填充F4及二硫化钼后还会进一步得到改善；PPS还具有一定的自润性。PPS的机械性能对温度的敏感性能小（3）热学性能：PPS具有***的热性能，短期可耐260℃，并可在200~240℃下长期使用；其耐热性与PI相当，仅次于F4塑料，这在热固性塑料中也不多见。