| 品牌：Ultramid | 是否进口：否 | 产地：德国 |
| 厂家(产地)：德国巴斯夫 | 牌号：A3EG7 | 销售方式：品牌经销 |
| 类型：标准料 | 品名：PA66 | 加工级别：注塑级 |
| 产品规格：25KG/包 | 产品特性：增强PA66 |
德国巴斯夫PA66 Ultramid A3EG7玻纤35%增强
Density / Specific Gravity | 1.41 | -- | g/cm | ASTM D792,*** 1183 |
Melt Volume-Flow Rate (MVR)(275°C/5.0 kg) | 40 | -- | cm/10min | *** 1133 |
Molding Shrinkage - Flow(3.18 mm) | 0.30 | -- | % | |
Water Absorption | ||||
Saturation | 5.0 | -- | % | ASTM D570 |
Saturation, 23°C | 5.0 | -- | % | *** 62 |
Equilibrium, 50% RH | 1.6 | -- | % | ASTM D570 |
Equilibrium, 23°C, 50% RH | 1.6 | -- | % | *** 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus(23°C) | 11500 | 8500 | MPa | *** 527-2 |
Tensile Strength | ||||
Break, 23°C | 207 | -- | MPa | ASTM D638 |
Break, 23°C | 210 | 150 | MPa | *** 527-2 |
Break, 80°C | 122 | -- | MPa | *** 527-2 |
Tensile Elongation | ||||
Break, 23°C | 3.0 | -- | % | ASTM D638 |
Break, 23°C | 3.0 | 5.0 | % | *** 527-2 |
Break, 80°C | 5.3 | -- | % | *** 527-2 |
Flexural Modulus | ||||
23°C | 9860 | -- | MPa | ASTM D790 |
23°C | 10000 | 8480 | MPa | *** 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | *** 179 | |||
-30°C | 12 | -- | kJ/m | |
23°C | 14 | 22 | kJ/m | |
Charpy Unnotched Impact Strength | *** 179 | |||
-30°C | 75 | -- | kJ/m | |
23°C | 95 | 110 | kJ/m | |
Notched Izod Impact | ||||
-40°C | 96 | -- | J/m | ASTM D256 |
23°C | 120 | -- | J/m | ASTM D256 |
23°C | 14 | -- | kJ/m | *** 180 |
汽车用***增强PA6复合材料制造发动机周边部件，如进气歧管、发动机罩盖等，可以代替传统金属材料，为了满足在发动机周边部件的使用要求，PA6材料应具备以下优点：
1). ***的强度和韧性，满足结构部件的机械性能
2).***耐热性，可以在高达130℃温度下连续使用
3). 长期的耐疲劳性，热老化后性能保持好
4). ***尺寸稳定性，具有防翘曲的效果
5). 表面效果好，无浮纤
6). 耐油性好，***性佳