30%玻纤PA6 TECHNYL C218LV30索尔维
Density | 1.35 | -- | g/cm | *** 1183/A |
Water Absorption(24 hr, 23°C) | 0.95 | -- | % | *** 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus(23°C) | 9700 | 6200 | MPa | *** 527-2/1A |
Tensile Strength | ||||
Break, 23°C | 160 | -- | MPa | ASTM D638 |
Break, 23°C | 165 | 120 | MPa | *** 527-2/1A |
Tensile Elongation | ||||
Break, 23°C | 3.0 | -- | % | ASTM D638 |
Break, 23°C | 3.8 | 4.5 | % | *** 527-2 |
Flexural Modulus | ||||
23°C | 8500 | -- | MPa | ASTM D790 |
23°C | 14300 | -- | MPa | *** 178 |
Flexural Strength(23°C) | 230 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 8.0 | -- | kJ/m | *** 179/1eA |
Charpy Unnotched Impact Strength(23°C) | 70 | -- | kJ/m | *** 179/1eU |
Notched Izod Impact(23°C) | 110 | -- | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
Heat Deflection Temperature | ||||
0.45 MPa, Unannealed | 220 | -- | °C | *** 75-2/Bf |
1.8 MPa, Unannealed | 205 | -- | °C | ASTM D648 |
1.8 MPa, Unannealed | 202 | -- | °C | *** 75-2/Af |
Melting Temperature | 222 | -- | °C | *** 11357-3 |
| Electrical | Dry | Conditioned | Unit | Test Method |
Volume Resistivity | 1.0E+15 | 1.0E+11 | ohms·cm | IEC 60093 |
Electric Strength(2.00 mm) | -- | 22 | kV/mm | IEC 60243-1 |
Relative Permittivity | 3.80 | 4.50 | IEC 60250 | |
Comparative Tracking Index(Solution A) | 550 | 475 | V | IEC 60112 |
汽车用***增强PA6复合材料制造发动机周边部件，如进气歧管、发动机罩盖等，可以代替传统金属材料，为了满足在发动机周边部件的使用要求，PA6材料应具备以下优点：
1). ***的强度和韧性，满足结构部件的机械性能
2).***耐热性，可以在高达130℃温度下连续使用
3). 长期的耐疲劳性，热老化后性能保持好
4). ***尺寸稳定性，具有防翘曲的效果
5). 表面效果好，无浮纤
6). 耐油性好，***性佳