| 品牌：TOYOLAC | 是否进口：否 | 产地：日本 |
| 厂家(产地)：日本东丽 | 牌号：450Y-X10 | 销售方式：品牌经销 |
| 类型：标准料 | 品名：ABS | 加工级别：注塑级 |
| 产品规格：25KG/包 | 产品特性：高耐热ABS |
日本东丽高耐热ABS TOYOLAC 450Y-X10
Density / Specific Gravity | 1.07 | g/cm | ASTM D792,*** 1183 |
Melt Mass-Flow Rate (MFR)(220°C/10.0 kg) | 6.0 | g/10 min | *** 1133 |
Molding Shrinkage - Flow | 0.50 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
Rockwell Hardness(R-Scale) | 111 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 2360 | MPa | *** 527-2/1 |
Tensile Strength | |||
Yield2 | 46.0 | MPa | ASTM D638 |
Yield | 53.0 | MPa | *** 527-2/50 |
Tensile Elongation | |||
Break2 | 12 | % | ASTM D638 |
Break | > 10 | % | *** 527-2/50 |
Flexural Modulus3 | 2300 | MPa | ASTM D790 |
Flexural Strength | |||
--3 | 77.0 | MPa | ASTM D790 |
--4 | 80.0 | MPa | *** 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 16 | kJ/m | *** 179/1eA |
Notched Izod Impact(23°C, 12.7 mm) | 150 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
1.8 MPa, Unannealed, 6.40 mm | 98.0 | °C | ASTM D648 |
1.8 MPa, Unannealed | 95.0 | °C | *** 75-2/A |
| Flammability | Nominal Value | Test Method | |
Flame Rating | HB | UL 94 |
塑料ABS的热变形温度为93~118℃，制品经退火处理后还可提高10℃左右。ABS在-40℃时仍能表现出一定的韧性，可在-40~100℃的温度范围内使用。塑料ABS的电绝缘性较好，并且几乎不受温度、湿度和频率的影响，可在大多数环境下使用。
塑料ABS也可以说是聚苯乙烯的改性，比HIPS有较高的抗冲击强度和更好的机械强度，具有良好的加工性能，可以使用注塑机、挤出机等塑料成型设备进行注塑、挤塑、吹塑、压延、层合、发泡、热成型，还可以焊接、涂覆、电镀和机械加工。ABS的吸水性比较高，加工前需进行干燥处理，干燥温度为70~85℃，干燥时间为2~6h；ABS制品在加工中容易产生内应力，如应力太大，致使产品开裂，应进行退火处理，把制件放于70~80℃的热风循环干燥箱内2~4h，再冷却至室温即可。