美国3M 粒径25微米PTFE DYNEON TFM 1705
Density / Specific Gravity | 2.16 | g/cm | ASTM D4894 |
Apparent (Bulk) Density | 0.42 | g/cm | ASTM D4894 |
Molding Shrinkage - Flow | 5.8 | % | ASTM D4894 |
Average Particle Size | 25 | m | ASTM D4894 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 650 | MPa | ASTM D638 |
Tensile Strength | 33.1 | MPa | ASTM D4894 |
Tensile Elongation(Break) | 450 | % | ASTM D4894 |
Deformation Under Load | ASTM D621 | ||
15 MPa2 | 9.00 | % | |
15 MPa3 | 10.0 | % | |
15 MPa4 | 4.50 | % |
| Thermal | Nominal Value | Unit | Test Method |
Melting Temperature | ASTM D4894 | ||
--5 | 317 to 337 | °C | |
--6 | 332 to 352 | °C | |
Service Temperature | -200 to 260 | °C |
| Electrical | Nominal Value | Unit | Test Method |
Dielectric Strength | 150 | kV/mm | ASTM D149 |
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating | V-0 | UL 94 |
PTFE的摩擦因数随滑动速率的增大而增大，当线速度达到0. 5一1. 0m/s以上时趋于稳定;而且静摩擦因数小于动摩擦因数，将这种特性用于轴承制造，可减小其起动阻力，使之从起动到运转都十分平稳。PTFE的摩擦因数随随载荷增加而减小，当载荷达到0. 8 MPa以上时趋于恒定。在高速、高载荷下，PTFE的摩擦因数低于0. 01。从***温到PTFE熔点，
其摩擦因数几乎不变，只有在表面温度高于熔点时，摩擦因数为才急剧增大。
由于分子间引力小，PTFE的硬度低，易被其他材料磨损。但是，只要对磨材料表面粗糙度合适，可在相当程度上降低PTEF的磨损量。