日本三菱耐候易脱模PC Iupilon S-2000VUR
Density | 1.20 | g/cm | *** 1183 |
Melt Mass-Flow Rate (MFR)(300°C/1.2 kg) | 10 | g/10 min | *** 1133 |
Melt Volume-Flow Rate (MVR)(300°C/1.2 kg) | 9.00 | cm/10min | *** 1133 |
Molding Shrinkage | Internal Method | ||
Across Flow | 0.50 to 0.70 | % | |
Flow | 0.50 to 0.70 | % | |
Water Absorption(Saturation, 23°C) | 0.24 | % | *** 62 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 2400 | MPa | *** 527-2/1 |
Tensile Stress(Yield) | 61.0 | MPa | *** 527-2/50 |
Tensile Strain | *** 527-2/50 | ||
Yield | 5.6 | % | |
Break | 110 | % | |
Flexural Modulus3 | 2300 | MPa | *** 178 |
Flexural Stress3 | 93.0 | MPa | *** 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 76 | kJ/m | *** 179 |
Charpy Unnotched Impact Strength(23°C) | No Break | *** 179 |
| Thermal | Nominal Value | Unit | Test Method |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 143 | °C | *** 75-2/B |
1.8 MPa, Unannealed | 129 | °C | *** 75-2/A |
Flame Rating | UL 94 | ||
0.38 mm | V-2 | ||
1.5 mm | V-2 | ||
3.0 mm | V-2 |