科思创(拜耳)高流动耐候PC Makrolon AL2447
MVR (300°C/1.2 kg) 19 cm/10 min; Automotive lighting; low viscosity; UV stabilized; easy release; injection molding - melt temperature 280 - 320°C; available in clear transparent colors and in various signal colors; headlamp lenses for automotive forward lighting
Density(23°C) | 1.20 | g/cm | ISO 1183 |
Apparent (Bulk) Density3 | 0.66 | g/cm | ISO 60 |
Melt Mass-Flow Rate (MFR)(300°C/1.2 kg) | 20 | g/10 min | ISO 1133 |
Melt Volume-Flow Rate (MVR)(300°C/1.2 kg) | 19 | cm/10min | ISO 1133 |
Tensile Modulus(23°C) | 2400 | MPa | ISO 527-2/1 |
Tensile Stress | |||
Yield, 23°C | 66.0 | MPa | ISO 527-2/50 |
Break, 23°C | 70.0 | MPa | ISO 527-2/5 |
Break, 23°C | 65.0 | MPa | ISO 527-2/50 |
Charpy Notched Impact Strength7 | ISO 179/1eA | ||
-30°C, Complete Break | 14 | kJ/m | |
23°C, Partial Break | 65 | kJ/m |
Heat Deflection Temperature | |||
0.45 MPa, Unannealed | 138 | °C | ISO 75-2/B |
1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
Glass Transition Temperature8 | 145 | °C | ISO 11357-2 |
PC塑胶原料的吸水率较大,加工***定要预热干燥,纯PC干燥120℃,改性PC一般用110℃温度干燥4小时以上。干燥时间不能超过10小时。一般可用对空挤出法判断干燥是否足够。再生料的使用比例可达20%。在某些情况下,可***的使用再生料,实际份量要视制品的品质要求而定。再生料不能同时混合不同的色母粒,否则会严重损坏成品的性质。