| 品牌：LEONA | 是否进口：否 | 产地：日本 |
| 厂家(产地)：日本旭化成 | 牌号：13G43 | 销售方式：品牌经销 |
| 类型：标准料 | 品名：PA66 | 加工级别：注塑级 |
| 产品规格：25KG/包 | 产品特性：增强PA66 |
日本旭化成43%玻纤PA66 Leona 13G43
Density / Specific Gravity | 1.50 | -- | g/cm | ASTM D792,*** 1183 |
Molding Shrinkage | Internal Method | |||
Across Flow | 0.70 | -- | % | |
Flow | 0.30 | -- | % |
Rockwell Hardness | ASTM D785,*** 2039-2 | |||
M-Scale | 96 | 80 | ||
R-Scale | 118 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus(23°C) | 12700 | 10200 | MPa | *** 527-2 |
Tensile Stress | ||||
Break, 23°C | 207 | 150 | MPa | *** 527-2 |
-- | 196 | 157 | MPa | ASTM D638 |
Charpy Notched Impact Strength | 12 | 18 | kJ/m | *** 179 |
Charpy Unnotched Impact Strength | 84 | 85 | kJ/m | *** 179 |
Notched Izod Impact | 130 | 210 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
Deflection Temperature Under Load | ||||
0.45 MPa, Unannealed | 260 | -- | °C | ASTM D648,*** 75-2/B |
1.8 MPa, Unannealed | 250 | -- | °C | ASTM D648 |
1.8 MPa, Unannealed | 255 | -- | °C | *** 75-2/A |
PA66 聚酰胺66或尼龙66化学和物理特性PA66在聚酰胺材料中有较高的熔点。它是一种半晶体-晶体材料。PA66在较高温度也能保持较强的强度和刚度。在产品设计时，一定要考虑吸湿性对几何稳定性的影响。为了提高PA66的机械特性，经常加入各种各样的改性剂。玻璃就是***常见的添加剂，有时为了提高抗冲击性还加入合成橡胶，如EPDM和SBR等。 PA66的粘性较低，因此流动性很好（但不如PA6）。