品牌:NORYL | 是否进口:否 | 产地:美国 |
厂家(产地):沙伯基础(原GE) | 牌号:HS2000X | 销售方式:品牌经销 |
类型:标准料 | 品名:PPO | 加工级别:注塑级 |
产品规格:25KG/包 | 产品特性:低翘曲PPO |
沙伯基础17%矿物增强PPE/PS NORYL HS2000X
PPE+PS blend. 17% Mineral reinforced. Non-brominated, non-chlorinated FR system. UL94 V0 and 5VA listing. UL746C f1. Radiant panel listing. Dielectric strength. Dimensional stability. Suitable for E/E market indoor/outdoor applications including electrical ceiling boxes and smoke detectors.
Density / Specific Gravity | 1.25 | g/cm | ASTM D792 |
Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
280°C/5.0 kg | 7.6 | g/10 min | |
300°C/5.0 kg | 7.6 | g/10 min | |
Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
280°C/5.0 kg | 6.00 | cm/10min | |
300°C/5.0 kg | 6.00 | cm/10min | |
Molding Shrinkage - Flow(3.20 mm) | 0.50 to 0.70 | % | Internal Method |
Outdoor Suitability | f1 | UL 746C |
Flexural Modulus | |||
50.0 mm Span4 | 3670 | MPa | ASTM D790 |
100 mm Span5 | 3550 | MPa | ASTM D790 |
-- | 3800 | MPa | ISO 178 |
Flexural Stress | |||
-- | 117 | MPa | ISO 178 |
Yield, 100 mm Span5 | 117 | MPa | ASTM D790 |
Break, 50.0 mm Span4 | 117 | MPa | ASTM D790 |
Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 10 | kJ/m | ISO 179/2C |
Notched Izod Impact | |||
23°C | 130 | J/m | ASTM D256 |
23°C6 | 9.0 | kJ/m | ISO 180/1A |
Unnotched Izod Impact(23°C) | 2200 | J/m | ASTM D4812 |
Reverse Notch Izod Impact(3.20 mm) | 810 | J/m | ASTM D256 |
Instrumented Dart Impact(23°C, Total Energy) | 443 | J | ASTM D3763 |
Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed, 3.20 mm | 117 | °C | ASTM D648 |
0.45 MPa, Unannealed, 6.40 mm | 128 | °C | ASTM D648 |
0.45 MPa, Unannealed, 4.00 mm, 100 mm Span7 | 126 | °C | ISO 75-2/Be |