| 品牌：Ultramid | 是否进口：否 | 产地：德国 |
| 厂家(产地)：德国巴斯夫 | 牌号：B3EG6 | 销售方式：品牌经销 |
| 类型：标准料 | 品名：PA6 | 加工级别：注塑级 |
| 特性级别：增强级 | 产品规格：25KG/包 | 产品特性：增强PA6 |
BASF 30GF增强PA6 Ultramid B3EG6
Density / Specific Gravity | 1.36 | -- | g/cm | ASTM D792,ISO 1183 |
Melt Volume-Flow Rate (MVR)(275°C/5.0 kg) | 50 | -- | cm/10min | ISO 1133 |
Molding Shrinkage - Flow(3.18 mm) | 0.30 | -- | % | |
Water Absorption | ||||
Saturation | 6.6 | -- | % | ASTM D570 |
Saturation, 23°C | 6.6 | -- | % | ISO 62 |
Equilibrium, 50% RH | 2.1 | -- | % | ASTM D570 |
Equilibrium, 23°C, 50% RH | 2.1 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus(23°C) | 9500 | 6200 | MPa | ISO 527-2 |
Tensile Strength | ||||
Break, 23°C | 172 | -- | MPa | ASTM D638 |
Break, 23°C | 185 | 115 | MPa | ISO 527-2 |
Tensile Elongation | ||||
Break, 23°C | 3.2 | -- | % | ASTM D638 |
Break, 23°C | 3.5 | 8.0 | % | ISO 527-2 |
Flexural Modulus | ||||
23°C | 8280 | -- | MPa | ASTM D790 |
23°C | 8600 | 5000 | MPa | ISO 178 |
Flexural Stress(23°C) | 270 | 180 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179 | |||
-30°C | 11 | -- | kJ/m | |
23°C | 15 | 30 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179 | |||
-30°C | 80 | -- | kJ/m | |
23°C | 95 | 110 | kJ/m | |
Notched Izod Impact | ||||
-40°C | 96 | -- | J/m | ASTM D256 |
23°C | 110 | -- | J/m | ASTM D256 |
23°C | 15 | 20 | kJ/m | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
Deflection Temperature Under Load | ||||
0.45 MPa, Unannealed | 220 | -- | °C | ASTM D648,ISO 75-2/B |
1.8 MPa, Unannealed | 210 | -- | °C | ASTM D648,ISO 75-2/A |
Peak Melting Temperature | 220 | -- | °C | ASTM D3418,ISO 3146 |