| 品牌：Ultramid | 是否进口：否 | 产地：德国 |
| 厂家(产地)：德国巴斯夫 | 牌号：B3EG3 | 销售方式：品牌经销 |
| 类型：标准料 | 品名：PA6 | 加工级别：注塑级 |
| 特性级别：增强级 | 产品规格：25KG/包 | 产品特性：增强PA6 |
巴斯夫15%玻纤增强PA6 Ultramid B3EG3
B3EG3典型应用于汽车后视镜外壳和山地自行车车轮。
Density / Specific Gravity | 1.23 | -- | g/cm | ASTM D792,ISO 1183 |
Melt Volume-Flow Rate (MVR)(275°C/5.0 kg) | 75 | -- | cm/10min | ISO 1133 |
Molding Shrinkage - Flow(3.18 mm) | 0.50 | -- | % | |
Water Absorption | ||||
Saturation | 7.7 | -- | % | ASTM D570 |
Saturation, 23°C | 7.7 | -- | % | ISO 62 |
Equilibrium, 50% RH | 2.3 | -- | % | ASTM D570 |
Equilibrium, 23°C, 50% RH | 2.3 | -- | % | ISO 62 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
Tensile Modulus(23°C) | 5800 | 3500 | MPa | ISO 527-2 |
Tensile Strength | ||||
Break, 23°C | 103 | -- | MPa | ASTM D638 |
Break, 23°C | 130 | 70.0 | MPa | ISO 527-2 |
Tensile Elongation | ||||
Break, 23°C | 3.5 | -- | % | ASTM D638 |
Break, 23°C | 3.5 | 15 | % | ISO 527-2 |
Flexural Modulus | ||||
23°C | 5170 | -- | MPa | ASTM D790 |
23°C | 5200 | 2500 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
Charpy Notched Impact Strength | ISO 179 | |||
-30°C | 7.0 | -- | kJ/m | |
23°C | 8.0 | 20 | kJ/m | |
Charpy Unnotched Impact Strength | ISO 179 | |||
-30°C | 45 | -- | kJ/m | |
23°C | 50 | 110 | kJ/m | |
Notched Izod Impact | ||||
-40°C | 48 | -- | J/m | ASTM D256 |
23°C | 59 | -- | J/m | ASTM D256 |
23°C | 6.0 | -- | kJ/m | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
Deflection Temperature Under Load | ||||
0.45 MPa, Unannealed | 215 | -- | °C | ASTM D648,ISO 75-2/B |
1.8 MPa, Unannealed | 190 | -- | °C | ASTM D648,ISO 75-2/A |
Peak Melting Temperature | 220 | -- | °C | ASTM D3418,ISO 3146 |