| 品牌：Pocan | 是否进口：否 | 产地：德国 |
| 厂家(产地)：德国朗盛 | 牌号：S1517 | 销售方式：品牌经销 |
| 类型：标准料 | 品名：PBT | 加工级别：注塑级 |
| 产品规格：25KG/包 | 产品特性：耐冲击PBT | 溶脂：27 |
Pocan S1517耐冲击PBT
Density(23°C) | 1.24 | g/cm | *** 1183 |
Apparent (Bulk) Density | 0.70 | g/cm | *** 60 |
Melt Volume-Flow Rate (MVR)(260°C/5.0 kg) | 27 | cm/10min | *** 1133 |
Molding Shrinkage | *** 294-4 | ||
Across Flow : 110°C, 2.00 mm3 | 0.30 | % | |
Across Flow : 260°C, 2.00 mm4 | 2.0 | % | |
Flow : 120°C, 2.00 mm3 | 0.30 | % | |
Flow : 260°C, 2.00 mm4 | 2.0 | % | |
Water Absorption | *** 62 | ||
Saturation, 23°C | 0.40 | % | |
Equilibrium, 23°C, 50% RH | 0.20 | % | |
| Hardness | Nominal Value | Unit | Test Method |
Ball Indentation Hardness | 90.0 | MPa | *** 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus(23°C) | 1900 | MPa | *** 527-1/1 |
Tensile Stress(Yield, 23°C) | 45.0 | MPa | *** 527-2/50 |
Tensile Strain(Yield, 23°C) | 5.1 | % | *** 527-2/50 |
Nominal Tensile Strain at Break(23°C) | > 50 | % | *** 527-2/50 |
Tensile Creep Modulus | *** 899-1 | ||
1 hr | 1650 | MPa | |
1000 hr | 1000 | MPa | |
Flexural Modulus5(23°C) | 2000 | MPa | *** 178/A |
Flexural Stress5 | *** 178/A | ||
23°C | 65.0 | MPa | |
3.5% Strain, 23°C | 60.0 | MPa | |
Flexural Strain at Flexural Strength6(23°C) | 5.8 | % | *** 178/A |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength | *** 179/1eA | ||
-30°C | 13 | kJ/m | |
23°C | 50 | kJ/m |