| 品牌：IUPITAL | 是否进口：否 | 产地：日本 |
| 厂家(产地)：日本三菱 | 牌号：F10-01 | 销售方式：品牌经销 |
| 类型：标准料 | 品名：POM | 产品规格：25KG/包 |
| 产品特性：高粘挤出级 |
高粘挤出级POM Iupital F10-01
Density | 1.41 | g/cm | *** 1183 |
Melt Mass-Flow Rate (MFR)(190°C/2.16 kg) | 2.5 | g/10 min | *** 1133 |
Melt Volume-Flow Rate (MVR)(190°C/2.16 kg) | 2.2 | cm/10min | *** 1133 |
Molding Shrinkage - Flow(3.00 mm) | 2.2 | % | Internal Method |
Water Absorption - 60% RH(23°C) | 0.22 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 2800 | MPa | *** 527-1/1 |
Tensile Stress(Yield) | 63.0 | MPa | *** 527-2/50 |
Tensile Strain | *** 527-2/50 | ||
Yield | 10 | % | |
Break | 33 | % | |
Flexural Modulus3 | 2500 | MPa | *** 178 |
Flexural Stress3 | 89.0 | MPa | *** 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 8.0 | kJ/m | *** 179 |
Charpy Unnotched Impact Strength(23°C) | 280 | kJ/m | *** 179 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Unannealed | 156 | °C | *** 75-2/B |
1.8 MPa, Unannealed | 100 | °C | *** 75-2/A |
Melting Temperature | 166 | °C | *** 11357-3 |
CLTE | *** 11359-2 | ||
Flow | 1.1E-4 | cm/cm/°C | |
Transverse | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
Electric Strength | IEC 60243-1 | ||
1.00 mm | 32 | kV/mm | |
3.00 mm | 19 | kV/mm | |
Dielectric Constant | IEC 60250 | ||
1 MHz | 3.90 | ||
100 MHz | 3.90 | ||
Dissipation Factor | IEC 60250 | ||
1 MHz | 7.0E-3 | ||
100 MHz | 2.0E-3 | ||
Comparative Tracking Index | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
Flame Rating(0.8 mm) | HB | UL 94 |