| 品牌：NOVADURAN | 是否进口：否 | 产地：日本 |
| 厂家(产地)：日本三菱 | 牌号：5810G40 | 销售方式：品牌经销 |
| 类型：标准料 | 品名：PBT | 加工级别：注塑级 |
| 特性级别：增强级 | 产品规格：25KG/包 | 产品特性：低翘曲PBT |
高耐热低翘曲PBT NOVADURAN 5810G40
Density | 1.53 | g/cm | *** 1183 |
Melt Volume-Flow Rate (MVR)(250°C/5.0 kg) | 26 | cm/10min | *** 1133 |
Molding Shrinkage | Internal Method | ||
Across Flow : 2.00 mm | 0.60 | % | |
Flow : 2.00 mm | 0.30 | % | |
Water Absorption(Saturation, 23°C) | 0.080 | % | *** 62 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 13000 | MPa | *** 527-1/1 |
Tensile Stress(Break) | 130 | MPa | *** 527-2/5 |
Tensile Strain(Break) | 1.0 | % | *** 527-2/5 |
Flexural Modulus2 | 12000 | MPa | *** 178 |
Flexural Stress2 | 195 | MPa | *** 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 11 | kJ/m | *** 179 |
Charpy Unnotched Impact Strength(23°C) | 60 | kJ/m | *** 179 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Annealed | 218 | °C | *** 75-2/B |
1.8 MPa, Annealed | 190 | °C | *** 75-2/A |
Melting Temperature | 224 | °C | *** 11357-3 |
CLTE | *** 11359-2 | ||
Flow : -30 to 35°C | 1.0E-5 | cm/cm/°C | |
Flow : -30 to 120°C | 1.0E-5 | cm/cm/°C | |
Flow : 35 to 120°C | 1.0E-5 | cm/cm/°C | |
Transverse : -30 to 35°C | 7.0E-5 | cm/cm/°C | |
Transverse : -30 to 120°C | 9.0E-5 | cm/cm/°C | |
Transverse : 35 to 120°C | 1.1E-4 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | 1.0E+16 | ohms | IEC 60093 |
Volume Resistivity | 1.0E+16 | ohms·cm | IEC 60093 |
Electric Strength | IEC 60243-1 | ||
1.00 mm | 40 | kV/mm | |
2.00 mm | 30 | kV/mm | |
Dielectric Constant(1 MHz) | 3.20 | IEC 60250 | |
Dissipation Factor(1 MHz) | 0.017 | IEC 60250 |