| 品牌：NOVADURAN | 是否进口：否 | 产地：日本 |
| 厂家(产地)：日本三菱 | 牌号：5010G45 | 销售方式：品牌经销 |
| 类型：标准料 | 品名：PBT | 特性级别：增强级 |
| 产品规格：25KG/包 | 产品特性：玻纤增强 |
45%玻纤增强PBT Novaduran 5010G45
Density | 1.67 | g/cm | *** 1183 |
Melt Volume-Flow Rate (MVR)(250°C/5.0 kg) | 15 | cm/10min | *** 1133 |
Molding Shrinkage | Internal Method | ||
Across Flow : 2.00 mm | 0.90 | % | |
Flow : 2.00 mm | 0.40 | % | |
Water Absorption(Saturation, 23°C) | 0.060 | % | *** 62 |
| Mechanical | Nominal Value | Unit | Test Method |
Tensile Modulus | 15000 | MPa | *** 527-1/1 |
Tensile Stress(Break) | 165 | MPa | *** 527-2/5 |
Tensile Strain(Break) | 2.0 | % | *** 527-2/5 |
Flexural Modulus3 | 14500 | MPa | *** 178 |
Flexural Stress3 | 260 | MPa | *** 178 |
| Impact | Nominal Value | Unit | Test Method |
Charpy Notched Impact Strength(23°C) | 14 | kJ/m | *** 179 |
Charpy Unnotched Impact Strength(23°C) | 60 | kJ/m | *** 179 |
| Thermal | Nominal Value | Unit | Test Method |
Deflection Temperature Under Load | |||
0.45 MPa, Annealed | > 220 | °C | *** 75-2/B |
1.8 MPa, Annealed | 209 | °C | *** 75-2/A |
Melting Temperature | 224 | °C | *** 11357-3 |
CLTE | *** 11359-2 | ||
Flow : -30 to 35°C | 1.5E-5 | cm/cm/°C | |
Flow : -30 to 120°C | 1.5E-5 | cm/cm/°C | |
Flow : 35 to 120°C | 1.0E-5 | cm/cm/°C | |
Transverse : -30 to 35°C | 6.8E-5 | cm/cm/°C | |
Transverse : -30 to 120°C | 1.0E-4 | cm/cm/°C | |
Transverse : 35 to 120°C | 1.3E-4 | cm/cm/°C | |
RTI Elec(0.75 mm) | 75.0 | °C | UL 746B |
RTI Imp(0.75 mm) | 75.0 | °C | UL 746B |
RTI Str(0.75 mm) | 75.0 | °C | UL 746B |
| Electrical | Nominal Value | Unit | Test Method |
Surface Resistivity | 5.0E+16 | ohms | IEC 60093 |
Volume Resistivity | 2.0E+16 | ohms·cm | IEC 60093 |
Electric Strength | IEC 60243-1 | ||
1.00 mm | 28 | kV/mm | |
2.00 mm | 25 | kV/mm | |
Dielectric Constant(1 MHz) | 3.40 | IEC 60250 | |
Dissipation Factor(1 MHz) | 0.016 | IEC 60250 | |
Comparative Tracking Index (CTI) | PLC 1 | UL 746A |